Polypropylene

Polypropylene Homopolymer

Virgin material produced by Petro Rabigh

grade description MFI 2.16 kg application
FS2011E homopolymer polypropylene intended for the extrusion of biaxially oriented film. It is easy to process and suitable for metallization. The film made from this resin exhibit excellent transparency, excellent mechanical and barrier properties 2.2 g/10 min food packaging,
printing lamination,
adhesive tape,
cigarette packaging,
metalized film
       
FS3011E homopolymer polypropylene intended for the extrusion of biaxially oriented film. It is easy to process and suitable for high speed BOPP line. The film made from this resin exhibit excellent transparency, excellent mechanical and barrier properties. It is also suitable for metallization 3.0 g/10 min food packaging,
printing lamination,
adhesive tape,
cigarette packaging,
metalized film
       
FY2011E homopolymer polypropylene intended for yarn extrusion. Yarn made from these resin exhibit excellent mechanical properties. It is also suitable for Thermoforming application 2.2 g/10 min woven sacks,
thermoforming,
monofilament,
strapping bands
       
FY3011E homopolymer polypropylene intended for yarn extrusion characterized by ease of processing and low heat shrinkage. Yarn made from this resin exhibit excellent mechanical property. It is also suitable for Thermoforming application 3.0 g/10 min woven sacks,
woven cloths,
binding tape,
monofilament
       
FY4012E homopolymer polypropylene intended for Yarn extrusion. Yarn made from this resin exhibits high denier strength, high anti splitting and low heat shrinkage 4.0 g/10 min woven sacks,
woven cloths,
binding tape,
monofilament
       
Y101 homopolymer polypropylene intended for injection molding applications. Molded part made from this resin exhibit high stiffness, good heat resistance and good flow characteristic 15 g/10 min general purpose,
housewares

Polypropylene Copolymer

Virgin material produced by Petro Rabigh

grade description MFI 2.16 kg application
AV161 block copolymer polypropylene formulated with nucleating agent and intended for general-purpose injection molding. Injection molding parts made from this resin exhibit high impact and high stiffness 5.5 g/10 min commodity,
battery,
containers,
chairs,
seat bottom
       
AW564 block copolymer polypropylene intended for industrial application. It is formulated with nucleating agent to enhance the stiffness. Injection molding parts made from this resin exhibit good impact, high stiffness and good heat stability 9.0 g/10 min crates,
battery,
industrial application,
electrical appliances,
chairs, seat bottom
       
AR564 block copolymer polypropylene intended for industrial application. It has a medium melt flow and formulated with nucleating agent to enhance the stiffness. Injection molding parts made from this resin exhibit good impact, high stiffness and good heat stability 24.5 g/10 min crates,
pails,
industrial application,
electrical appliances
       
AR764 block copolymer polypropylene intended for industrial application. It has a medium melt flow and formulated with nucleating agent and anti-static. Injection molding parts made from this resin exhibit good impact, high stiffness and good heat stability 24.5 g/10 min crates,
pails,
industrial application,
electrical appliances
       
AZ564G block copolymer polypropylene intended for industrial application & thin wall applications. It has a high melt flow and formulated with nucleating agent. Injection molding parts made from this resin exhibit good impact, high stiffness and good heat stability 39 g/10 min crates,
thin wall application,
industrial application,
electrical appliances
       
AZ764 block copolymer polypropylene intended for industrial application & thin wall applications. It has a high melt flow and formulated with nucleating agent and antistatic. Injection molding parts made from this resin exhibit good impact, high stiffness and good heat stability 39 g/10 min crates,
thin wall application,
industrial application,
electrical appliances